It is a new type nonflammable material made of lightweight materials. It's formed by a variety of inorganic materials
after the chemical reaction. It's made from magnesium oxide, magnesium chloride, fly ash , plant fiber etc.
SPECIFICATIONS FOR MGO HOLLOW PANEL | |||
Length | 2200mm-3600mm | ||
Thickness | 75mm/90mm/100mm/120mm/150mm/200mm | ||
Width | 600mm | ||
Standard size | 2800mm*600mm | ||
Hole diameter | 40mm for 75/120mm, 60mm for 90/100/150/200mm | ||
Bending load (board weight ratio) | 2.7-3.6 | ||
Compressive strength (Mpa) | 3.7-4.3 Mpa | ||
Softening coefficient | 0.82-0.86 | ||
Moisture content (%) | 10-11% | ||
Drying shrinkage value (mm/m) | 0.4-0.5mm/m | ||
It is a new type nonflammable material made of lightweight materials. It's formed by a variety of inorganic materials
after the chemical reaction. It's made from magnesium oxide, magnesium chloride, fly ash , plant fiber etc.
SPECIFICATIONS FOR MGO HOLLOW PANEL | |||
Length | 2200mm-3600mm | ||
Thickness | 75mm/90mm/100mm/120mm/150mm/200mm | ||
Width | 600mm | ||
Standard size | 2800mm*600mm | ||
Hole diameter | 40mm for 75/120mm, 60mm for 90/100/150/200mm | ||
Bending load (board weight ratio) | 2.7-3.6 | ||
Compressive strength (Mpa) | 3.7-4.3 Mpa | ||
Softening coefficient | 0.82-0.86 | ||
Moisture content (%) | 10-11% | ||
Drying shrinkage value (mm/m) | 0.4-0.5mm/m | ||