Magnesia Panel Glass Magnesite Magnesium Board Flooring

Raw Material

MGO board is made of high purity magnesium oxide, MGO sulfate (Mgso4)

replace of magnesium chloride(Mgcl2),high strength fiber glass mesh, perlite, non-woven fabrics.

Key advantages

  • Fireproof Waterproof

  • No asbestos sweating

  • Suitable for light steel frame

  • Insulate against heat and Keep warm

Availability:
Quantity:
  • MgSo4 Board
  • OCM
Product Name

magnesia panel glass magnesite magnesium board



Raw Material


MGO board is made of high purity magnesium oxide, MGO sulfate (Mgso4)

replace of magnesium chloride(Mgcl2),high strength fiber glass mesh, perlite, non-woven fabrics.

Key advantages

  • Fireproof Waterproof

  • No asbestos sweating

  • Suitable for light steel frame

  • Insulate against heat and Keep warm


Specifications


magnesia panel glass magnesite magnesium board is a newly developed type of incombustible inorganic board on the basis of the traditional magnesium oxide board.It is manufactured from 100% mineral components and recycled water It is also called fireproof board or Mgo sulfate board.

Item Thickness Size Backside Color
External wall 10-12mm 1220*2400/2700/3000mm Textile/sanded

white

grey

green

yellow

blue

black

Flooring board 15-16-18-20-22mm 600*1200/2400/2700/3000mm Textile/sanded
Ceiling board 3-4.5-6mm 600/1200mm*600mm/1200mm Textile/sanded
Interior board 6-8-9-10mm 1220*2440/2700/3000mm Textile/sanded
Edges type  

magnesia panel glass magnesite magnesium board customized size and types are available.

  
Certifications

1.Bending strength

Test item

Test Method

Test Result

Bending strength

AS/NZS 2908.2:2000 Section 8.1.2.1

Direction

Modulus of rupture

Machine direction

13.8MPa

Across machine direction

12.6MPa

Average

13.2MPa

Remark

Specimen Dimensions:250mm*250mm*10mm,10pcs

2.Water permeability

Test item

Test Method

Test Result

Water permeability

AS/NZS 2908.2:2000 Section 8.2.2

Specimen

Test Result

1

No formation of drops of water on underside of the sheet

2

No formation of drops of water on underside of the sheet

3

No formation of drops of water on underside of the sheet

Remark

Specimen Dimensions:600mm*600mm*10mm,3pc

3. Mositure movement

Test item

Test Method

Test Result

Mositure movement

ASTM C1185-08(R2016)Section8

Specimen

Linear change(%)

Machine direction

0.18

Across machine direction

0.12

Average

0.15

Remark

Specimen Dimensions:76mm*05mm*10mm,1pcs per direction

4.Falling Ball Impact

Test item

Test Method

Test Result/Observation

Falling Ball Impact

ASTM D1037-12 Section 21

Bottom surface crack at 900mmheight. Top surface crack at 950mm height

Remark

Impactor :steel ball

Impactor mass: 535 g

Impactor diameter: 51 mm

OCM®products all certificated according to ASTM and AU/NZS standards. More information please contact us

FAQ

1.What is your delivery time?

15-20days after down payment.


2.What is your payment?

TT30% as down payment and balance after B/L.Or irrevocable LC.


3.Can you do customized product?

Yes.We can cut any sizes as required.


4.What is your company production capacity?

We can produce 20,000sqm per day.


5.What is your Minimum Order Quantity,Can we order mixing different sizes?

Yes.MOQ 100pcs and mixed loading also acceptable.


Previous: 
Next: 

Fill in the following information,Our sales will contact you!

Product

Product

Quick Link

Service

Oriental Construction Material Industry Co., Ltd.(ChinaOCM) is located in Zhangjiagang city, Jiangsu province, china. We are a comprehensive enterprise combining researching, manufacturing and processing magnesia products.
 Copyright  2022 Oriental Construction Material (SuZhou) Co.,Ltd      Sitemap